[1]涂浩,周圣洁,陈小春,等.热浸镀锌中铁-铝-锌渣回收工艺研究[J].常州大学学报(自然科学版),2016,(06):73-77.[doi:10.3969/j.issn.2095-0411.2016.06.014]
　TU Hao,ZHOU Shengjie,CHEN Xiaochun,et al.Study on the Recovering Process of Hot Dipping Fe-Al-Zn Slag[J].Journal of Changzhou University(Natural Science Edition),2016,(06):73-77.[doi:10.3969/j.issn.2095-0411.2016.06.014]
点击复制

热浸镀锌中铁-铝-锌渣回收工艺研究()
分享到：

常州大学学报(自然科学版)[ISSN:2095-0411/CN:32-1822/N]

卷:
期数:
2016年06期
页码:
73-77
栏目:
材料科学与工程
出版日期:
2016-11-30

文章信息/Info

Title:
Study on the Recovering Process of Hot Dipping Fe-Al-Zn Slag
作者:
涂浩; 周圣洁; 陈小春; 苏旭平
1. 常州大学 材料科学与工程学院,江苏 常州 213164; 2. 江苏省材料表面科学与技术重点实验室,江苏 常州 213164; 3. 江苏省光伏科学与工程协同创新中心,江苏 常州 213164
Author(s):
TU Hao1; 2; 3;  ZHOU Shengjie1; 2; 3;  CHEN Xiaochun1; 2;  SU Xuping1; 2; 3
1. School of Materials Science and Engineering, Changzhou University, Changzhou 213164, China; 2. Jiangsu Key Laboratory of Materials Surface Science and Technology, Changzhou 213164, China; 3. Jiangsu Collaborative Innovation Center of Photovolatic Scien
关键词:
铁铝锌渣;  熔炼温度;  静置时间;  回收率;  回收工艺
Keywords:
Fe-Al-Zn slag;  melting temperature;  standing time;  recovery;  recycling process
分类号:
X 781.1
DOI:
10.3969/j.issn.2095-0411.2016.06.014
文献标志码:
A
摘要:
针对铁铝锌渣的回收过程,研究了熔炼温度、静置时间以及添加剂对粗锌回收率和主要成分的分布规律的影响。研究表明,采用(质量分数)50% NaCl+25% KCl+25% CaF2 覆盖剂对熔池进行保护,并用渣重0.3%～0.5%的ZnCl2除渣工艺可使粗锌直收率达到73%。450 ℃二次除渣静置工艺可以有效提高粗锌品质,粗锌中的铁、铝(质量分数)分别从一次除渣工艺的0.089%和0.485%降至0.022%和0.228%。
Abstract:
Aiming at the recycling process of the Fe-Al-Zn slag,the influence of the melting temperature, standing time and additives on recovery of zinc and the distribution of the main elements have been investigated.The results show that the recovery of zinc can achieve 73% by protecting the covering agent and adding ZnCl2 which weighted 0.3～0.5 percent of slag in the bath. It can significantly improve the quality of zinc, the mass fraction of iron and aluminum in the zinc ingot from 0.089%and 0.485% to 0.022% and 0.228% by removing and holding for the second time at 450 ℃.

参考文献/References:

[1]何小凤, 李运刚, 陈金,等. 高效热镀锌废渣处理炉设计研究[J]. 中国有色冶金, 2015, 44(1):39-43.
[2]WEI DS, TU H, ZHOU S J, et al. Effect of silicon on the reaction between solid and liguid Zn-22.3% Al bareh. Surface & Coatings Technology, 2016, 305:29-35.
[3]何小凤, 李运刚, 陈金. 热镀锌渣锌灰回收处理工艺评述[J]. 中国有色冶金, 2008(2):55-58.
[4]NAKANO J, MALAKHOV D V, YAMAGUCHI S, et al. A full thermodynamic optimization of the Zn-Fe-Al system within the 420-500 degrees temperature range[J]. Calphad the International Research Journal for Calculation of Phase Diagrams, 2007, 31(1):125-140.
[5]彭浩平,苏旭平,王建华,等. 热浸镀锌铝的界面反应机理[J]. 中国有色金属学报, 2012, 22(11):3168-3175.
[6]GHOSH G. Aluminium-Iron-Zinc[M]// Iron Systems, Part 1. Springer Berlin Heidelberg, 2008:319-348.
[7]李尚谦. 从热镀锌渣中回收锌[J]. 四川冶金, 1983(3):83-87.
[8]张伟, 窦传龙, 匡立春,等. 一种锌及锌基合金熔铸用造渣剂:CN1730197[P]. 2006-02-08.
[9]李广田, 陈敏, 杜成武. 钢铁冶金辅助材料[M]. 北京:化学工业出版社, 2009:53-55.

备注/Memo

备注/Memo:
收稿日期:2016-08-25。基金项目:国家自然科学基金资助项目(51271040, 51271041)。作者简介:涂浩(1965—),男,湖南湘潭人,博士,副教授。 通讯联系人:苏旭平(1961—),E-mail: sxping@cczu.edu.cn
更新日期/Last Update: 2016-11-20