[1]谢爱娟,罗士平,陶宇炜,等.γ-MnO2/海泡石-凹凸棒土低温脱硝催化剂研究[J].常州大学学报(自然科学版),2018,30(04):19-27.[doi:10.3969/j.issn.2095-0411.2018.04.004]
 XIE Aijuan,LUO Shiping,TAO Yuwei,et al.Study on the Catalyst of γ-MnO2/ Sepiolite-Attapulgite for Low Temperature Denitration[J].Journal of Changzhou University(Natural Science Edition),2018,30(04):19-27.[doi:10.3969/j.issn.2095-0411.2018.04.004]
点击复制

γ-MnO2/海泡石-凹凸棒土低温脱硝催化剂研究()
分享到:

常州大学学报(自然科学版)[ISSN:2095-0411/CN:32-1822/N]

卷:
30
期数:
2018年04期
页码:
19-27
栏目:
化学化工
出版日期:
2018-07-28

文章信息/Info

Title:
Study on the Catalyst of γ-MnO2/ Sepiolite-Attapulgite for Low Temperature Denitration
作者:
谢爱娟1罗士平1陶宇炜2屠美倩1
1. 常州大学 石油化工学院,江苏 常州 213164; 2. 常州大学 信息化建设与管理中心,江苏 常州 213164
Author(s):
XIE Aijuan1 LUO Shiping1 TAO Yuwei2 TU Meiqian1
1. School of Petrochemical Engineering, Changzhou University, Changzhou 213164 China; 2. Center of Information Development and Management, Changzhou University, Changzhou 213164 China
关键词:
海泡石 凹凸棒土 γ-MnO2 选择性催化还原 NOx转化率
Keywords:
sepiolite attapulgite γ-MnO2 selective catalytic reduction NOx conversion
分类号:
X 831
DOI:
10.3969/j.issn.2095-0411.2018.04.004
文献标志码:
A
摘要:
采用天然的海泡石(Sepiolite, SEP)和凹凸棒土(Attapulgite, ATP)复合作为催化剂载体,负载活性组分γ-MnO2,从而制备一系列γ-MnO2/SEP-ATP复合催化剂,并应用于低温氨选择性催化还原脱硝技术。同时对优选的催化剂进行了抗SO2性能、N2选择性吸附以及稳定性测试。结果表明,当γ-MnO2/SEP中掺杂了ATP时,催化剂表面的Br?nsted酸位普遍提高,促进了催化剂对NH3的吸附。活性测试结果表明,当γ-MnO2质量分数为7%、海泡石和ATP质量比为1:1时,催化剂的脱硝效果最佳, 在150 ℃就能达95%以上。证明SEP与ATP的复合不仅能提升γ-MnO2的低温活性,同时也可以有效地保护催化剂。
Abstract:
Using natural sepiolite(SEP)and attapulgite(ATP)as a co-catalyst carrier, γ-MnO2 was loaded onto the surface of SEP-ATP to obtain a series of γ-MnO2/SEP-ATP catalysts, which was further applied in the denitration technology of NH3 selective catalytic reduction(NH3SCR)for low temperature. Meanwhile, the anti-SO2 performance, N2 selective adsorption and stability test for optimized catalysts were also carried out. The results indicated that when ATP was doped in the γ-MnO2/SEP, the Br?nsteds on the surface of the catalyst were generally increased, which could promote the adsorption of NH3. The activity test results illustrated that when the mass fraction of γ-MnO2 was 7%, and the mass ratio of SEP and ATP was 1:1, the denitration effect of the catalyst was the best, and the NOx conversion could reach over 95% at 150 ℃. It is proved that the combination of SEP and ATP can not only improve the low-temperature activity of the γ-MnO2, but also effectively protect the catalyst.

参考文献/References:


[1] LI J, CHANG H, MA L, et al. Low-temperature selective catalyticreduction of NOx with NH3 over metal oxide and zeolite catalysts-a review[J]. Catalysis Today, 2011, 175: 147-156.
[2]FORZATTI P, NOVA I, TRONCONI E, et al. Enhanced NH3 selective catalytic reduction for NOx abatement[J]. Angewandte Chemie, 2009, 121: 8516-8518.
[3]XIONG S C, LIAO Y, XIAO X, et al. The mechanism of the effect of H2O on the low temperature selective catalytic reduction of NO with NH3 over Mn-Fe spinel[J]. Catalysis Science & Technology, 2015, 5: 2132-2140.
[4]ZHANG L Y, SHI L, HUANG L, et al. Rational design of high-performance DeNOx catalysts based on MnxCo3-xO4 nanocages derived from metal-organic frameworks[J]. ACS Catalysis, 2014, 4: 1753-1763.
[5]DAHLIN S, NILSSON M, B?CKSTR?M D, et al. Multivariate analysis of the effect of biodiesel-derived contaminants on V2O5-WO3/TiO2 SCR catalysts[J]. Applied Catalysis B: Environmental,2016, 183: 377-385.
[6]SONG L Y, CHAO J D, FANG Y J, et al. Promotion of ceria for decomposition of ammonia bisulfate over V2O5-MoO3/TiO2 catalyst for selective catalytic reduction[J]. Chemical Engineering Journal, 2016, 303: 275-281.
[7]MARTINJ A, YATES M, AVILA P, et al.Nitrous oxide formation in Low temperature selective catalytic reduction of nitrogen oxides with V2O5/TiO2 catalysts[J]. Applied Catalysis B: Environmental, 2007, 70(1/2/3/4):330-334.
[8]SHAO D,LIU G F,QING H.Study on catalytic decomposition of dioxins by supported CeO2-TiO2-V2O5 composite Cataly[J].Journal of Rare Earths,2007,25:232-235.
[9]QI G S, YANG R T. Low-temperature selective catalytic reduction of NO with NH3 over iron and manganese oxides supported on titania[J]. Applied Catalysis B:Environmental, 2003, 44(3): 217-225.
[10]QI G S,YANG R T.Characterization and FTIR studies of MnOx-CeO2 catalyst for low-temperature selective catalytic reduction of NO with NH3[J].Journal of Physical Chemistry B,2004,108(40):15738-15747.
[11]QI G S, YANG R T, CHANG R.MnOx-CeO2 mixed oxides prepared by co-precipitation for selective catalytic reduction of NO with NH3 at low temperatures[J].Applied Catalysis B:Environmental,2004,51(2):93-106.
[12]LUO S P, ZHOU W T, XIE A J, et al. Effect of MnO2 polymorphs structure on the selective catalytic reduction of NOx with NH3 over TiO2-Palygorskite[J]. Chemical Engineering Journal, 2016, 286: 291-299.
[13]金胜明,阳卫军,唐谟堂.海泡石表面改性及其应用试验研究[J].非金属矿,2001,24(4):23-25.
[14]张良, 姚超, 蒋凯, 等. 凹凸棒土有机表面改性的工艺研究[J]. 江苏工业学院学报. 2008, 20(1): 9-12.
[15]关媛, 王少莽, 易广, 等. 酸化凹凸棒石的制备及其对苯胺的吸附性能[J]. 常州大学学报(自然科学版),2017, 29(6): 15-25.
[16]CAI S X, HU H, LI H R, et al. Design of multi-shell Fe2O3@MnOx@ CNTs for the selective catalytic reduction of NO with NH3: improvement of catalytic activity and SO2 tolerance[J]. Nanoscale, 2016, 8: 3588-3598.
[17]WANG X, ZHENG Y, XU Z, et al.Amorphous MnO2 supported on carbon nanotubes as a superior catalyst for low temperature NO reduction with NH3[J]. RSC Advance, 2013, 3(29):11539-11542.
[18]SULTANA A, SASAKI M, HAMADA H. Influence of support on the activity of Mn supported catalysts for SCR of NO with ammonia[J]. Catalysis Today, 2012, 185: 284-289.
[19]LI Y, LI Y P, WANG P F, et al. Low-temperature selective catalytic reduction of NOx with NH3 over MnFeOx nanorods[J].Chemical Engineering Journal, 2017, 330: 213-222.
[20]XIE A J, ZHOU X M, HUANG X Y, et al. Cerium-loaded MnOx/attapulgite catalyst for the low-temperature NH3-selective catalytic reduction[J]. Journal of Industrial and Engineering Chemistry, 2017, 49: 230-241.

相似文献/References:

[1]周 轶,韶 晖,吴琦刚,等.无机陶瓷膜提纯凹凸棒石粘土的工艺[J].常州大学学报(自然科学版),2012,(04):16.
 ZHOU Yi,SHAO Hui,WU Qi-gang,et al.Study on Purification of Attapulgite with Inorganic Ceramics Membranes[J].Journal of Changzhou University(Natural Science Edition),2012,(04):16.
[2].2007年总目次[J].常州大学学报(自然科学版),2007,(04):65.
[3]马文中,潘霁,龚方红,等.凹凸棒土对聚偏氟乙烯结晶行为的影响[J].常州大学学报(自然科学版),2016,(06):57.[doi:10.3969/j.issn.2095-0411.2016.06.011]
 MA Wenzhong,PAN Ji,GONG Fanghong,et al.The Effect of Attapulgite on Crystallization Behavior of Poly(vinylidene fluoride)[J].Journal of Changzhou University(Natural Science Edition),2016,(04):57.[doi:10.3969/j.issn.2095-0411.2016.06.011]

备注/Memo

备注/Memo:
基金项目:江苏省重点研发计划(BE2016654); 常州市科技支撑计划(CE20165022)。
作者简介:谢爱娟(1968—)女,江苏武进人,硕士,高级实验师。 E-mail:xaj@cczu.edu.cn
更新日期/Last Update: 2018-07-30