[1]董 亮,吴 桐,姚知林,等.硫酸铜参比电极用多孔陶瓷头的制备与性能[J].常州大学学报(自然科学版),2021,33(03):9-16.[doi:10.3969/j.issn.2095-0411.2021.03.002]
　DONG Liang,WU Tong,YAO Zhilin,et al.Preparation and Properties of Porous Ceramic Head for Copper Sulfate Reference Electrode[J].Journal of Changzhou University(Natural Science Edition),2021,33(03):9-16.[doi:10.3969/j.issn.2095-0411.2021.03.002]
点击复制

硫酸铜参比电极用多孔陶瓷头的制备与性能()
分享到：

常州大学学报(自然科学版)[ISSN:2095-0411/CN:32-1822/N]

卷:
第33卷
期数:
2021年03期
页码:
9-16
栏目:
材料科学与工程
出版日期:
2021-05-28

文章信息/Info

Title:
Preparation and Properties of Porous Ceramic Head for Copper Sulfate Reference Electrode
文章编号:
2095-0411(2021)03-0009-08
作者:
董 亮;  吴 桐;  姚知林;  石超杰;  赵会军
(常州大学 石油工程学院, 江苏 常州 213164)
Author(s):
DONG Liang;  WU Tong;  YAO Zhilin;  SHI Chaojie;  ZHAO Huijun
(School of Petroleum Engineering, Changzhou University, Changzhou 213164, China)
关键词:
参比电极;  多孔陶瓷;  孔径;  孔隙率
Keywords:
reference electrode;  porous ceramic;  pore size;  porosity
分类号:
TB 321
DOI:
10.3969/j.issn.2095-0411.2021.03.002
文献标志码:
A
摘要:
以滑石粉为主要原料, 通过调节原料粒径、 烧成温度、 黏合剂用量、 成型压力和烧成方式等参数, 制备了多种硫酸铜参比电极(CSE)用多孔陶瓷头。测试分析了多孔陶瓷头的孔隙率、 孔径及形貌结构、 收缩率等性能参数, 选取3种多孔陶瓷头制作了便携式硫酸铜参比电极并测试了其电极电位长期稳定性及寿命。结果表明, 原料粒径、 烧成温度、 成型压力对多孔陶瓷头的孔径和孔隙率影响较大, 随着原料粒径的减小、 烧成温度的增加、 成型压力增大, 孔径和孔隙率随之减小; 采用孔径约为522 nm、 孔隙率为17.4%的多孔陶瓷头制作的便携式参比电极的电极电位长期稳定性较好, 通过计算估算寿命可达4.2 a。
Abstract:
Selecting talcum powder as the main raw material, porous ceramic heads for copper sulfate reference electrode(CSE)were prepared by adjusting the parameters of raw material size, sintering temperature, binder content, molding pressure and sintering mode. The porosity, pore size, morphology, structure, shrinkage and other performance parameters of the porous ceramic heads were tested and analyzed. Three kinds of porous ceramic heads were selected to make a portable copper sulfate reference electrode, and the long-term stability and life of the electrode potential were tested. The results show that the size of raw material, sintering temperature and forming pressure have a significant influence on the pore size and porosity of porous ceramic head. With the decrease of the size of raw material, the increase of sintering temperature and forming pressure, the pore size and porosity decrease. The electrode potential of the portable reference electrode made of porous ceramic head with pore size of 522 nm and porosity of 17.4% has a long-term stability and the estimated life can reach 4.2 years.

参考文献/References:

[1]胡士信. 阴极保护工程手册[M]. 北京: 化学工业出版社, 1999.
[2]黄永昌. 电化学保护技术及其应用:第九讲 阴极保护测量技术[J]. 腐蚀与防护, 2000, 21(11): 523-528.
[3]曲本文, 刘兴章, 陈志强, 等. 国内参比电极现状简述[J]. 全面腐蚀控制, 2017, 31(6): 25-27, 34.
[4]许可望. 长效硫酸铜参比电极及氧化物阳极的新材料研究[D]. 北京: 中国石油大学(北京), 2007.
[5]阮景红, 刘国, 王修云, 等. 塔河油田油气管线阴极保护系统失效原因与对策[J]. 腐蚀与防护, 2012, 33(3): 261-264.
[6]曲远方. 功能陶瓷及应用[M]. 2版. 北京: 化学工业出版社, 2014.
[7]方邺森, 方金满. 陶瓷矿物原料: 滑石[J]. 硅酸盐通报, 1984, 3(2): 52-57.
[8]诸爱珍. 滑石瓷的烧结问题及解决办法[J]. 山东陶瓷, 2003, 26(6): 29-32.
[9]刘维良. 先进陶瓷工艺学[M]. 武汉: 武汉理工大学出版社, 2004.
[10]张云洪. 陶瓷工艺技术[M]. 北京: 化学工业出版社, 2006.
[11]王洪生. 滑石瓷老化的成因及其对策[J]. 江苏陶瓷, 1998, 31(2): 28-31.
[12]刘培生, 马晓明. 多孔材料检测方法[M]. 北京: 冶金工业出版社, 2006.
[13]许祥在, 翟秋兰. 多孔材料的孔径分布与渗透性测定[J]. 分析仪器, 1999, 30(4): 48-52.
[14]宝鸡有色金属研究所. 粉末冶金多孔材料: 下册[M]. 北京: 冶金工业出版社, 1978.
[15]阮建明, 黄培云. 粉末冶金原理[M]. 北京: 机械工业出版社, 2012.

备注/Memo

备注/Memo:
收稿日期:2020-10-15。
基金项目:国家自然科学青年基金资助项目(51401017); 江苏省研究生实践创新计划(SJCX19_0671)。
作者简介:董亮(1983—), 男, 河南信阳人, 博士, 高级工程师。E-mail: dongliang@cczu.edu.cn
更新日期/Last Update: 1900-01-01