聚氨酯微球功能材料的制备与表征()
分享到：

常州大学学报(自然科学版)[ISSN:2095-0411/CN:32-1822/N]

卷:
期数:
2000年01期
页码:
29-33
栏目:
出版日期:
2000-03-25

文章信息/Info

Title:
Preparation and Characterization of Polyurethane Microsphere
作者:
付荣兴1 ;  岳　倩2 ;  沈介发1 ;  付劲松;  夏汉中3
1.江苏石油化工学院精细化工设计研究所, 江苏 常州 213016
Author(s):
FU Rong -xing 1 ;  YUE Qian ;  SHEN Jie -fa 1 ;  FU Jin -song ;  XIA Han -zhong
1 .Department of Fine Chemical , Jiangsu Institute of Pet rochemical Technology , Changzhou 213016 , China
关键词:
聚氨酯; 微球; 反相悬浮聚合
Keywords:
polyurethane ; microspheres ; counter -phase suspension polymerization
分类号:
T Q 425.23
文献标志码:
A
摘要:
以聚醚多元醇(635) 及多苯基多亚甲基多异氰酸酯(PAPI) 为原料, 在液体石蜡和CaCO3 中进行反相悬浮聚合, 制成 了聚氨酯微球。考察了分散剂种类及用量、异氰酸酯与羟基的比例、聚合温度、搅拌速度等因素对成球的影响。用DSC 法测定 了微球的T g 、Td , 测定了200 ℃下的失重率。通过BET 法测定了微球的压碎强度、耐酸碱性及耐溶剂性。证明了用本法所合 成的PU 微球有较好的抗耐性, 较高的抗压强度和较好的吸附性能。
Abstract:
Polyuretane microspheres based on polyether polyols (635)and PAPI w ere prepared by counter - phase suspension polymerization in liquid w ax and CaCO3 .The effects of species and doses of dispersers , polymericat ion temperature , rate of w hip on the formation of microspheres w ere inspected .The Tg and Td of the microspheres were determined by DSC method , and ratio of weight loss at 200 ℃w ere tested , too .The specific surface areas of micropheres , the diameter and the volume of pore and curve of adsorpt ion and desorption w ere determined by BET method .The crushing strength , acid , base and solvent resistance of the micropheres w ere tested .It has proved that the PU micropheres prepared by this method have hig h resistance , hig h crushing strength and good adsorbability .

参考文献/References:

〔1〕Anjaneyulu Y, Marayya R, Rao R Prabhakara.Removal and Recovery of Priority Pollutan t Phenols f rom Indust rial Eff luent s Using PU Foam Medium 〔J〕.Oil C ham Pollut , 1990 , 7 (4):349 - 365 .
〔2〕付荣兴.聚氨酯微孔材料在的石油化学工业中的应用〔J〕. 石油化工, 1996 , 25 (2):134 -137 .
〔3〕马建明, 吴海坪.含羧基聚氨酯树脂微粒的制备及性能的研究 〔J〕.离子交换与吸附, 1996 , 12 (1):34 -38 .
〔4〕苏致兴, 彭银成, 高金城, 等.球形大孔聚氨酯树脂的合成及 形态研究〔J〕.高分子材料科学与工程, 1990.1 , 34 -38 .
〔5〕何炳林, 史作清.具有精细结构的吸附与离子交换树脂〔J〕. 应用化学, 1993 , 10 (5):1-6 .
〔6〕史林启, 郭贤权, 何炳林, 等.多嵌积聚氨酯大孔共聚物的制 备〔J〕.离子交换与吸附, 1995, 11 (5):424 -430 .
〔7〕黄少铭, 吴立芬, 靳亚非, 等.聚氨酯微球的合成及其表征 〔J〕.聚氨酯工业, 1999 , 14 (1):17 -21 .
〔8〕高正中.实用催化〔M〕.北京:化学工业出版社, 1996.201 -312 .

备注/Memo

备注/Memo:
作者简介:付荣兴:(1940-), 男, 江西清江人, 主要从事聚氨酯材料的合成;2.本院高分子材料系95 届毕业生; 3 .本院高分子材料系91 届毕业生。
更新日期/Last Update: 2000-03-25