[1]赵　斌,沈　洁,徐娟燕.黑碳钢表面超细Al2O3 粒子的 复合化学镀铜工艺的探讨[J].常州大学学报(自然科学版),2002,(02):19-22.
　ZHAO Bin,SHEN Jie,XU Juan -y an.Electroless Composite Copper Plating of Al2O3 Ultraf ine Powders on Carbon Steels[J].Journal of Changzhou University(Natural Science Edition),2002,(02):19-22.
点击复制

黑碳钢表面超细Al2O3 粒子的 复合化学镀铜工艺的探讨()
分享到：

常州大学学报(自然科学版)[ISSN:2095-0411/CN:32-1822/N]

卷:
期数:
2002年02期
页码:
19-22
栏目:
出版日期:
2002-06-25

文章信息/Info

Title:
Electroless Composite Copper Plating of Al2O3 Ultraf ine Powders on Carbon Steels
作者:
赵　斌1 ;  沈　洁1 ;  徐娟燕
1.华东理工大学化学系, 上海200237
Author(s):
ZHAO Bin1 ;  SHEN Jie1 ;  XU Juan -y an
1 .Department of Chemist ry , East China University of Science and Technology , Shanghai 200237 , China
关键词:
超细Al2O3 ; 复合化学镀铜; 镀速; 耐磨性; 抗氧化性
Keywords:
Al2O3 ult rafine pow ders ; electroless composite copper plating ; plating rate ; anti -wear ; anti - o xidat ion
分类号:
T Q 153.14
文献标志码:
A
摘要:
探讨了黑碳钢表面上的超细Al2O3 粒子的复合化学镀铜工艺, 研究了镀液的温度、pH 值、镀液中Al2O3 粒子的含量等因 素对复合化学镀铜性能的影响, 结果是镀液温度70 ℃、pH 值13.0 、Al2O3 含量为6 g/ L 镀层质量最好。并检测了复合镀层的 抗氧化性、耐磨性及镀层与基体的结合力, 与铜镀层作比较, 其抗氧化性、耐磨性能均有提高。通过激光散射粒度仪进行 Al2O3 粒子的粒度分布测试及扫描电镜对镀层表面形貌的观察, 并采用XRD 对镀层进行定性分析, 确认Al2O3 微粒已成为复合 镀
Abstract:
In this paper , the reaction conditions of electroless composite copper plating of Al2O3 ultraf ine powders on carbon steels have been studied .The ef fects of the bath temperature , pH value and the concent ration of Al2O3 on plating properties have been discussed .The results show that the opt imum composite Al2O3 -Cu plating layer can be got w hen bath temperature is 70 ℃, pH value is 13.0 , the co ncent ration of Al2O3 is 6 g/L , and the load is A/ V =60 cm2/L .Meanw hile , the abili ties of the anti -oxidation and anti -w ear , the strength between metal basis and plating layer have been measured .The result s show that the ant i -o xidat ion and anti -wear of Al2O3 -Cu layers are bet ter than those of the Cu layer′s .Moreover , the size dist ribution of Al2O3 ult rafine powders is determined by laser -diffusion apparatus, and the appearance of composite plating layer by SEM .The XRD analysis shows that Al2O3 pow ders have successfully entered the platinglayer .

参考文献/References:

[1] 姜晓霞, 沈伟.化学镀理论及实践[M] .北京:国防工业出 版社, 2000 .
[2] 阎洪.现代化学镀镍和复合镀新技术[M] .北京:国防工业 出版社, 1999 .
[3] 郭鹤桐, 张三元.复合镀层[M] .天津:天津大学出版社, 1991.
[4] 许强龄.镀(涂) 层质量检验技术[M] .上海:上海科学技 术文献出版社, 1992.
[5] 赵斌, 毛宇.氧化锌、氧化亚锡的复合化学镀铜[J] .华东 理工大学学报, 2000 , 26 (3):318 -321.
[6] 赵斌, 乐臻, 秦长勇.S nO2 超细粒子复合化学镀铜的研究[J] .化学世界, 2002 , 43 (4):171 -174.

备注/Memo

备注/Memo:
作者简介:赵斌(1942 -), 女, 安徽人, 教授, 研究方向:金属及其化合物或合金的超微粒子分散液和粉体的制备 及应用以及复合化学镀的研究。
更新日期/Last Update: 2002-06-25