文章信息/Info

Title:
Study on Preparation and U V- ray Shieding Property of Nano sized TiO2 in the Rutile Phase
作者:
姚 超1;  2;  吴凤芹2 ;  林西平2;  汪 信1
1.南京理工大学化工学院, 江苏 南京 210094; 2.江苏工业学院, 江苏 常州 213016
Author(s):
YAO Chao 1;  2 ;  WU Feng- qin 2 ;  LIN Xi- ping 2 ;  WANG Xin 1
1. School of Chemical Engineering, Nanjing University of Science & Technology, Nanjing 210094, China
关键词:
纳米TiO2;  金红石;  粒径;  紫外线屏蔽;  透明性
Keywords:
nanoscale T iO2;  rut ile;  particle size;  UV- ray shieding;  t ransparency
分类号:
T B 383
文献标志码:
A
摘要:
以四氯化钛为原料, 低温合成了金红石型纳米T iO2 聚集体, XRD 和TEM 表明, 这种聚集体是由更小的T iO2 微晶组合 而成。聚集体经过不同温度的热处理, 制得不同粒径的纳米T iO2 颗粒, 结果显示, 当热处理在500 ℃ 以下时, 是T iO2 纳米晶 相互熔合成纳米颗粒的过程。当热处理在600 ℃ 以上时, 纳米TiO2 粒子快速长大。在波长200~ 800 nm 光区测定了纳米TiO2 分散液的透光率, 详细研究了纳米TiO2 粒径、含量和分散时间对紫外线的屏蔽效果和可见光透明性的影响。
Abstract:
The nanoscale ag gregate of TiO2 in the rutile phase was synthesized by using titanium tet rachloride as source material at room temperature. XRD and TEM revealed that the aggreg ate was composed of much tinier nanocrystalline of TiO2. The different particle size of nanosized T iO2 was obtained at dif ferent temperatures of heat treatment. Results showed when the temperature of heat treatment was lower than 500℃, it was the process of melt ing nanocrystalline of T iO2 with nanometer particle. While the temperature of heat t reatment was higher than 600℃ , the primary particle of nanoscale T iO2 grew rapidly. Transmittance ofdispersion of nanosized TiO2 had been tested between 200- 800 nm. The effect of particle size, content , heat t reatment and dispersing time on U V- ray shieding property and transparency of visible light was investigated in detail.

参考文献/References:

[1] 徐良, 步平1 防晒化妆品及其市场发展[J] 1 日用化学品科 学, 1997, 20 ( 2) : 17- 20.
[2] 涂国荣, 王武尚, 张利兴, 等1 纳米TiO2 与天然紫外吸收剂 防晒效用的研究[J] 1 精细化工, 2001, 18 ( 7) : 379- 381.
[3] 罗付生, 韩爱军1 化妆品用聚甲基丙烯酸甲酯- 二氧划钛复合 微球的制备及性能[J] 1 日用化学工业, 2002, 32 ( 2) : 41 - 43.
[4] Ogawa Kat suki, Takata Sadaki, Kumagaya Shigenori. Cosm etic Composition Containing Spindle Shaped Fine Part icles of T itanium Dioxide [P] . US : 6123927, 2000- 09- 26.
[5] McCaulley, James A, Hubbard Michael A. Transparent Barrier Coatings Ex hibit ing Reduced Thin Film Interferen ce [P] . US : 6051296, 2000- 04- 18.
[6] 沈钟, 王国庭1 胶体与表面化学[M] 1 北京: 化学工业出版 社, 19971 40- 45.

备注/Memo

备注/Memo:
基金项目: 江苏省/ 九五0 科技攻关资助项目( NO. BG 98010- 1) 作者简介: 姚超( 1969- ) , 男, 安徽怀远人, 博士研究生, 研究方向: 纳米材料制备及表面处理。
更新日期/Last Update: 2003-09-25