无卤阻燃HDPE/MVQ/EPDM共混材料的研究()
分享到：

常州大学学报(自然科学版)[ISSN:2095-0411/CN:32-1822/N]

卷:
期数:
2012年01期
页码:
24-28
栏目:
出版日期:
2012-01-01

文章信息/Info

Title:
Study of Hologen-Free Flame Retardant HDPE/MVQ/EPDM Blends
作者:
陶国良; 李 靖; 沈 清; 纪波印; 刘 涌
常州大学 材料科学与工程学院,江苏 常州 213164
Author(s):
TAO Guo-liang; LI Jing; SHEN Qing; JI Bo-yin; LIU Yong
School of Materials Science and Engineering, Changzhou University, Changzhou 213164, China
关键词:
无卤阻燃;  多元共混;  电缆料;  耐高温
Keywords:
hologen-free flame retardant;  multi-component blends;  cable compound;  high temperature
分类号:
TQ 316.64
文献标志码:
A
摘要:
选用高密度聚乙烯(HDPE)/甲基乙烯基硅橡胶(MVQ)/三元乙丙橡胶(EPDM)为基材,研究了MH用量、表面改性和阻燃剂复配,以及交联剂等对共混体系力学性能和阻燃性能的影响。结果表明:γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH570)对MH改性效果较好,可有效提高MH与基体的相容性。MH/APP复配阻燃体系具有协同作用,比例为55/15 时LOI最高。2,5-二甲基-2,5-双(过氧化叔丁基)己烷(KMP-C8)作为交联剂其用量2.0 phr最佳。
Abstract:
The selection and compounding of high density polyethylene(HDPE), methyl vinyl silicone rubber(MVQ)and ethylene propylene diene monomer(EPDM)as base polymers are studied, in which the effect of surface modification and composite of flame retardant, dosage of crosslinking agent and so on on the properties was further investigated. Results indicated that silane coupling agent(KH570)could increase compatibility of MH in basic resin. The result of LOI showed there was synergistic action in MH/APP composite flame retardant and its optimal proportion was 55/15. The optimal dosage of crosslinking agent(KMP-C8)was 2.0 phr.

参考文献/References:

[1]郭建华,曾幸荣.白色填料对氟橡胶/硅橡胶共混胶性能的影响[J].有机硅材料,2010,24(6):337-431.
[2]甘泉,戚嵘嵘.环氧树脂增强耐高温聚乙烯电缆材料的制备[J].工程塑料应用,2009,37(12):42-45.
[3]周素蓉.125 ℃辐射交联阻燃聚烯烃电缆料的研制[D].北京:北京化工大学,2000.
[4]Morrell S H.Review of the effects of surface treatments on polymer-filler interactions[J].Plastic and Rubber Processing and Applications,2007,24(1):179-182.
[5]俞振海,卢晗锋,梁锦,等.硅烷偶联剂对氢氧化镁表面改性及其在聚丙烯中的应用[J].无机盐工业,2010,42(2):12-14.
[6]刘继纯,高喜平,刘红宇,等.Mg(OH)2表面处理对阻燃PP性能的影响[J].塑料科技,2009,37(2):46-49.
[7]GU J W,ZHANG G C,DONG S L,et al.Study on preparation and fire-retardantmechanisms analysis of intumescent coatings[J].Sur Coat Technol,2007,201(18):7 835-7 841.
[8]宋成伟,韩志东,赵洪.无卤阻燃聚烯烃化学交联反应动力学研究[J].现代塑料加工应用,2007,19(5):31-34.
[9]张洪波,吕明福,张师军.过氧化物交联HDPE材料的研究[J].合成树脂及塑料,2007,23(4):43-46.
[10]徐晓峰,汪传斌,王松明,等.GB/T12706-2008 额定电压1 kV(Um=1.2 kV)到35 kV(Um=40.5 kV)挤包绝缘电力电缆及附件[S].北京:中国标准出版社,2008.
[11]贾少晋,张志成,徐相凌,等.γ辐照制备耐高温阻燃电缆材料的研究[J].辐射研究与辐射工艺,2000,18(2):117-122.

备注/Memo

备注/Memo:
作者简介:陶国良(1958-),男,江苏溧阳人,教授,主要从事高分子材料高性能化研究和废旧橡胶绿色回收工艺技术及应用等。
更新日期/Last Update: 2012-01-01